XOANONS® Dispersant in solvent-based
Model number
XOANONS®LD 1152
Materialization index
|
Item |
Index |
Test the method or the equipment |
criterion of detection |
|
Composition |
Modified styrene maleic anhydride polymer |
--- |
--- |
|
Appearance |
Orange transparent liquid |
--- |
--- |
|
Solid content |
≥95% |
Electric drying oven |
GB/T 1725-2007 |
|
Density |
1.02-1.06 g/ml |
Specific gravity cup |
GB/T 6750-2007 |
|
Viscosity |
1000-3000mPa·s |
Digital rotational viscometer |
GB/T 1723-1993 |
|
pH value |
6-8 |
glass electrode method |
GB/T 9724-2007 |
|
Refractive index |
1.458-1.462 |
Abbe refractometer |
GB/T 6488-2008 |
Note: This indicator only represents the typical results, and is not regarded as a specification, mainly with specific COA.
Application area
Dispersion of various inorganic powders in solvent-based
Key property
?Provide spatial hindrance effect. Adding it to inorganic powder slurry, especially nickel powder slurry, can significantly reduce the viscosity of the slurry and increase the solid content of the slurry;Improve the fluidity of the slurry.
?Reduce adverse phenomena such as sedimentation and flocculation of the slurry; The storage stability of the slurry is good.
Incorporation
Add LD 1152 to the solvent and stir well to dissolve. Then add it to the slurry according to the formula and grind and disperse it together. The suitability of the dispersant system can be determined based on the dispersed particle size and viscosity of the slurry.
Suggested addition
Addition amount (purchase form) for inorganic powder: 1-10%
Storage stability
Seal and store away from light. Unopened in the original package for 24 months. Products beyond the storage period can continue to be used after passing the inspection. The container is not fully used and unprecedented, and must be closed immediately after use.
Package
25kg (plastic drum)